Summary:Our objective is to develop accurate measurement methods for the nanoscale stress distributions and surface defects that control device performance and reliability (performance over service life) in microelectronic and micro and nanoelectromechanical systems (MEMS and NEMS). Such methods will enable manufacturing processes to be optimized for device performance and lifetime, and address a critical measurement need in the MEMS industry, i.e., 90 % of MEMS customers require a demonstration of device reliability, but only 50 % of vendors provide one. Description:
Impact and Customers:
Major Accomplishments:Stress measurement by Raman scattering is based on measuring the shift of Raman phonon bands in materials under stress. A CRM scattering system has been developed with state-of-the-art stress and spatial resolution. Automated peak fitting routines enable shifts in the 522 cm-1 Raman peak in Si to be measured with approximately 0.02 cm-1 uncertainty, corresponding to measurement-limited stress precision of about 10 MPa (strains of about 10-4). Scans consisting of 128 x 128 hyperspectral arrays range from wide area, 150 µm x 150 µm, to small area, 5 µm x 5 µm, the latter giving rise to a pixel spacing of 40 nm. Each spectrum takes about 1 second, enabling a high resolution stress map to be generated in about 4 hr. Measurement development has focused principally on three aspects (using single-crystal Si test vehicles): (i) identification and quantification of the stress “signatures” of controlled, contact-induced defects in Si using micro- and nano-indentation techniques; (ii) verification of the scalar (tensor-averaged) piezospectroscopic coefficients through comparison with EBSD measurements, using the known stress distributions of indentation flaws and their associated cracks; and (iii) determination of the limits of the technique for measuring stress variations in engineered structures. Examples of (i) are shown in the figures on the previous page, which show rendered stress maps of a three-sided Berkovich nanoindentation on a Si(111) surface, spherical nanoindentations on Si(111), a four-sided Vickers microindentation on Si(001), and a linear wedge nanoindentation on Si(001) (top to bottom on the page, respectively). Red and blue indicate compressive and tensile stress, respectively, and the different signatures of the fracture and deformation patterns for the various defects are obvious: such information can be used to predict the behavior of the defects under subsequent loading.
CRM and EBSD stress profiles across a wedge indentation in Si
Progress in (ii) has been marked by the quantitative agreement obtained between CRM and EBSD measurements, largely through the ability to probe different depths beneath a sample surface using different Raman excitation light, as shown in the stress profile figure for the wedge indentation. Stress measurement by EBSD is based on distortion of the diffraction pattern by strain in the crystalline lattice. A cross-correlation method has been developed that compares high-quality diffraction patterns (such as in the example figure) obtained from scanning electron microscope scans
![]() EBSD pattern used for strain mapping of Si
and produces stress maps with stress and spatial resolution comparable to those obtained with CRM. Agreement between the two methods was shown to be exact when surface-localized blue excitation was used for the CRM measurement. Arrays of indentations aligned along different crystallographic directions were used in (iii) and an example is shown in the next figure. Clear differences in the local stress fields of the spherical indentations are visible. ![]() Raman stress map of a stress-engineered Si surface
|
![]() End Date:ongoingLead Organizational Unit:mmlStaff:Stephan Stranick (CSTL) Associated Products:Project Summary (PDF) Contact
Lawrence Friedman |