PORTLAND CEMENT (TOTAL DUST) IN WORKPLACE ATMOSPHERES
Method Number: | ID-207 |
|
Matrix: | Air filter and bulk material |
|
OSHA Permissible Exposure Limits
Portland Cement (PC)
Final Rule Limits:
Transitional Limit: |
Expressed as Time-Weighted Averages (TWA)
10 mg/m3 Total Dust
5 mg/m3 Respirable Dust (See Section 1.)
50 mppcf |
|
Collection Procedure: | Total dust air samples are collected on tared
5-µm pore size, 37-mm diameter polyvinyl chloride (PVC) filters.
The air samples are post-weighed and submitted to the laboratory when total dust
exposures exceed 10 mg/m3. A bulk sample consisting of 10 to 20 mL of
Portland cement is collected to serve as reference material for laboratory quantitation. |
|
Recommended Air Volume: | 240 L |
|
Recommended Sampling Rate: TWA Determinations: |
1 L/min for total dust air samples |
|
Analytical Procedure: | Samples are quantitatively analyzed and qualitatively
identified by X-ray techniques. Standards are prepared from the bulk material.
Suspensions of the samples are deposited onto Ag membrane filters and quantitatively analyzed
by measuring X-ray fluorescence (XRF) intensities for Ca, Si, Fe, and Sr in PC and
by measuring the attenuation of X rays from the fluorescing Ag membrane filter. For qualitative
confirmation, the common PC crystalline solid phases in the bulk and air sample dusts are
compared using X-ray diffraction. |
|
Detection Limits: |
11 to 640 µg PC [Detection limits depend upon interferences present (See Sections
1.3.1. and 4.2.1.).]
| |
Precision and Accuracy
Validation Levels:
CVT (pooled):
Bias:
Overall Analytical Error: |
0.6 to 7.7 mg total dust (See comments in Section 1.3.) 0.114 0.001 ±22.9% |
|
Method Classification: | Validated Analytical Method |
Chemist: | Mike C. Rose |
Date: | May, 1991 |
Commercial manufacturers and products mentioned in this method are
for descriptive use only and do not constitute endorsements by USDOL-OSHA.
Similar products from other sources can be substituted.
Branch of Inorganic Methods Development
OSHA Salt Lake Technical Center
Salt Lake City, Utah
1. Introduction
This method describes the sampling and analysis of industrial hygiene total dust air
samples for unfinished Portland cement (PC).
General industry often expresses the composition of materials derived from minerals as simple
oxides. This convention is useful in accounting for the elemental composition of PC, but it
does not describe the actual compounds present. Using this convention, the four major PC
components are CaO, SiO2, Al2O3,
and Fe2O3. In terms of these hypothetical
components, the approximate composition of PC is as follows:
CaO | 59 to 75% |
SiO2 | 17 to 28% |
Al2O3 + Fe2O3 |
4 to 20% |
|
Total | ~100% |
(See Reference 5.1. for a ternary phase diagram that more clearly portrays
the stoichiometric oxide composition of PCs.)
Typical PC compositions also include the minor elements Cr, Zn, F, Mn, P, Sr, Na, Ti, K, Mg, and S
with concentrations ranging from 0.01 to several percent, respectively (5.2.).
In chemical terms, the two essential major components in PC are tricalcium silicate
(Ca3SiO5) and dicalcium silicate
(Ca2SiO4)
(5.3.-5.5.). Additional compounds
commonly present in PC include alumina (Al203),
tricalcium aluminate (Ca3Al2O6),
iron oxide (Fe2O3) and calcium aluminum
ferrite (Ca4Al2Fe2O10)
(5.1., 5.5., 5.6.).
The manufacture of PC involves heating together specifically selected ground minerals to give
the desired composition of PC. The heating process produces chunks of PC called clinker. To
produce commercial grade PC, the PC clinker is usually ground with a small amount of the
calcium-containing mineral gypsum (CaSO42H2O)
to control the rate of setting (5.1.-5.3.).
The PC composition and particle-size distribution determine how the material sets
up after water is added.
In crystallographic terms, Portland cement is a complex mixture; the amount of each solid phase
present depends on the starting composition, thoroughness of mixing, firing conditions, and the
thermal history of the material. At least 22 different solid phases have been identified.
Unstable solid phases can persist at room temperature; for example, PC has six distinct alite
polymorphs (i.e., different Ca3SiO5
crystalline solid phases) - each stable at a different temperature range; the presence of
impurities in PC allow three alite polymorphs to coexist at room temperature (5.1.).
Portland cement has negligible vapor pressure, negligible aqueous solubility and a variable
composition. Typical bags of commercial "Portland cement" also contain additives. Because
Portland cement is a mixture and not a single compound, a representative pure bulk sample
of the PC material must be collected at the time of air sampling for laboratory use to resolve
this variability in composition. The bulk sample defines the particular PC composition to which
the employee is exposed. Air samples are collected to determine personal exposures. Due to the
variable elemental composition of PC, this method analyzes several elements by X-ray
fluorescence (XRF) to quantitatively evaluate PC exposures. Due to the variable crystalline
composition this method qualitatively assesses whether crystalline PC phases are present by
X-ray diffraction (XRD).
The following flow chart indicates the recommended treatment of these samples:
Portland cement air samples
This method concentrates on total dust sampling; respirable samples can also be taken to assess
compliance to the OSHA 5 mg/m3 respirable dust PEL. Respirable PC
exposures are determined gravimetrically in the field by the compliance officer or industrial
hygienist. The respirable dust PEL for PC is identical for most respirable dusts, and any
exceptions (e.g., quartz and vanadium pentoxide) are lower than 5 mg/m3.
At the present time, there is no need to verify that respirable dust air samples consist only of
PC. However, these respirable PC dust samples can be submitted to the laboratory for quartz
analysis because quartz is a potential contaminant in PC. Refer to the quartz method
(5.7.) for the appropriate respirable quartz dust sampling procedure.
If the laboratory analyzing the samples has a controlled environment where the relative humidity
(RH) is less than 80%, the XRD qualitative verification step may be performed prior to XRF
quantitation. See Section 3. for procedural variations.
As previously mentioned, commercial PCs are complex mixtures. Each PC component has different
physical properties. Portland cement is ground in the final stage of manufacture; therefore,
one can expect different particle-size distributions for each component. When
suspended in the air, the resulting differential settling of components may significantly
contribute to variation in the analytical results. To compensate for the expected variation
in sampling, several different analyses are performed. Samples and standards are quantitatively
analyzed for PC based on Ca, Si, Fe, and Sr by XRF. The Ca and Si are major constituents occurring
in the two essential calcium silicates present in PC. The trace elements Fe and Sr are in the
raw materials used to produce the PC clinker; therefore, assessments of these elements also
provide useful estimates for PC content. In addition, the X-ray fluorescence from
the Ag membrane filter is used for a mass absorption (MA) analysis of the samples. By measuring
the attenuation of X rays from the fluorescing Ag membrane filter, the overall mass of the sample
can be determined. Analysis by MA is sensitive to the mean composition of the sample. Due to the
potential for outliers among the five quantitative analyses, the median result of the five is
the most representative measure of PC content.
Because of the potential for interferences, qualitative confirmation is a necessary step.
After the XRF analyses, the prepared total dust air samples and bulk reference samples are
resubmitted for qualitative verification using XRD to confirm the presence of PC crystalline
solid phases. The total dust and bulk samples are also screened for quartz using OSHA Method
ID-142
(5.7.). Quartz is usually a minor but common component In PC. The results
for quartz analyses of total dust and bulk samples are approximate. If the PC material contains
more than 1% quartz, the PEL for quartz should be considered and respirable dust samples
should be obtained (5.5.).
The elements Ca, Si, Fe, and Sr are widely distributed in the environment; therefore, the
identification of these elements does not provide conclusive confirmation of the presence of
PC. Also, mass absorption analysis by XRF provides no qualitative information. For these
reasons, analytical results are reported only when there is both general quantitative
agreement and qualitative XRD verification of the PC crystalline solid phases.
1.1. History
1.1.1. The previous PEL for PC was 50 million particles per cubic foot (mppcf) which required an
impinger sampling method for collection. Analysis was performed by particle counting using light
microscopy. The 50 mppcf PEL was equivalent to approximately 15 mg/m3.
This level is the same as for particulates not otherwise regulated; therefore, the exposure
could be evaluated gravimetrically. The PEL was changed in 1989 to 10 mg/m3
due to the irritant status of PC and so that gravimetric methods could be used by industrial
hygienists to monitor employee exposures (5.5.). The
10 mg/m3 level, however, is less than the nuisance dust level of
15 mg/m3 and entails identification to verify PC content. The PC
phases can not be identified either gravimetrically or by light microscopy.
1.1.2. Classical wet-chemical techniques have been applied to the elemental
analysis of PC (5.2., 5.8.). Due to limited
sensitivity, these techniques are not optimal for the quantitation of low-mass
air samples obtained in industrial hygiene monitoring. These wet-chemical
techniques are destructive to the sample and do not offer phase identification. Although it is
possible to prepare samples first for phase identification and then destructively analyze the
sample by a wet method, this would involve tedious sample preparation.
1.1.3. Atomic absorption spectroscopy (AAS) offered a potential alternative method that might
be adapted for low-mass air samples (5.9.). However, the
identification of PC phases introduces the same complications noted in Section 1.1.2.
1.1.4. Another quantitative method investigated was a collaborative study with West Germany's
Saarbergwerke Aktiengesellschaft (SA) (5.10.) using their XRD technique.
Well-characterized reference materials were provided by SA. The SA XRD method
required reference materials that have particle-size distributions comparable to
the air samples. Potential interferences had been thoroughly identified. It was determined that
the SA XRD method was appropriate for respirable dust samples, but problems may arise when
attempting to quantify PC content in total dust samples. However, the XRD method was considered
a suitable technique to confirm the presence of PC in total dust samples.
1.1.5. The XRD and XRF portions of this method were evaluated using the equipment described
in Section 4.
1.2. Principles
1.2.1. X-ray fluorescence relies upon the excitation of atoms in a sample by the
application of X rays of sufficient energy to cause the promotion of inner orbital electrons
and subsequent decay accompanied by characteristic X-ray fluorescence.
In an energy-dispersive X-ray fluorescence (EDXRF) spectrometer, the
selected energy scale (or energy span) is divided up into smaller divisions called channels in
order to provide adequate energy resolution. Each channel represents an X-ray
energy having a small range of values. For example, in a multichannel analyzer (MCA) having
1,000 channels, the central channel would represent X-ray energies between 5.000
and 5.010 kV when the MCA is calibrated 10 kV full scale. During an analysis, the energy of
each detected X-ray photon is measured. Those photons having energies within the
selected energy scale are counted by incrementing the channel in the MCA that corresponds to
the measured energy. The line spectra resulting from X-ray fluorescence are
broadened into peaks by the limited ability of the spectrometer to resolve X-ray
photon energies. The peak shape approximates a normal (so-called Gaussian)
distribution. When plotted as a function of energy, the count data result in a spectrum after
sufficient counts are accumulated. Profile-fitting (deconvolution) computer
software can be used to determine net counts from peak areas or to resolve instances of
interferences due to peak overlaps.
The approximate relationship between an element's atomic number and the energy of individual
emission lines for each specific X-ray line series (e.g., the
Ka line or the
Lb line) is given by Moseley's law:
E = a(Z - s)2
Where:
E = energy of X ray
a = proportionality constant
Z = atomic number
s = constant for each line series
Moseley's law indicates that an element's spectral lines are a smooth function of the atomic
number. The spectral lines for elements with low atomic number (light elements) occur at lower
energies than the corresponding lines for elements with high atomic number (heavy elements).
The peak energies and spectral group patterns provide for qualitative identification.
1.2.2. Quantitation by XRF is tailored for thin layer dust samples redeposited on Ag membrane
filters. For uniform thin deposits, EDXRF produces signal intensities that are
proportional to the amount of analyte present. Matrix effects are normally minimal for such
samples; however, non-linear calibration curves can be used to correct for the
fluorescing Ag support medium, shadowing of particles in Ag membrane filter pores, and
particle-size effects. Calibration curves are further discussed in Appendix A.
Low-energy X rays are more strongly absorbed in thin layer samples than are high-energy
X rays. The MA analysis in this method uses the attenuation of low-energy X rays
(L series) arising from the fluorescing Ag membrane filter to determine sample mass. The
fluorescence X rays from the Ag membrane filter blanks are unattenuated by sample; therefore,
blanks have higher counts than the air samples in this kind of analysis and are more prone to
counting error. To improve the analytical accuracy in the MA analysis, three blanks (two
field blanks and one lab blank) are used.
1.2.3. The X-ray diffraction technique is based on the Bragg equation:
nl = 2d sinq
Where: |
n = | order of diffracted beam (usually 1) |
l = | wavelength of the monochromatic X-ray beam (Å) |
d = | distance between diffracting planes (Å) |
q = | angle between incident X-rays and the diffracting planes (in degrees) |
Note: | Most X-ray diffractometers are designed to scan using degrees
two-theta (2q). All 2q
angle references in this method assume a copper anode X-ray tube and a wavelength of ~1.54 Å.
|
Each crystalline substance has a unique repeating structure that extends in various directions
throughout the crystal. As a result of this periodicity, crystalline substances have atoms that
lie in planes parallel to one another which can participate in diffracting incident X rays.
The unique repeating structure can thus be probed with X rays to determine the set of
diffraction spacings (d-spacings) that uniquely characterize each substance.
During X-ray diffraction analyses, the angle (measured as
2q) is stepped in small increments. At each increment, the
diffractometer pauses to count the diffracted X rays for a specified period of time. A
diffraction pattern is produced by stepping the diffraction angle over a wide range. Because
powder samples of crystalline substances present essentially all orientations to the
X-ray beam, diffraction peaks from each different diffracting plane are
reproducibly represented in the diffraction pattern.
1.2.4. Two examples of experimentally determined PC XRD patterns are included in
Appendix B. Each PC has a different mixture of crystalline phases and each
Ca-containing phase is subject to differing amounts of ion-exchange
with Mg and Sr. Because Mg and Sr have ionic radii that differ from Ca, the
ion-exchange results in variations in d-spacings that are evidenced
by peak shifts in the pattern. For this reason, the experimentally determined patterns may
differ from those found in published pattern libraries for pure crystalline phases. The
pattern for each PC is unique and may be used like a fingerprint to identify it.
1.3. Method Performance
Two different PC standard reference materials, SRM 635 and SRM 637, were obtained from the
National Institute of Standards and Technology (NIST). These were used to evaluate method
performance. The detection limit (DL), recovery (R), coefficients of variation (CV and
CVT), and overall error (OE) data were determined.
1.3.1. Method detection limits
The detection limits for Si-, Ca-, and MA-based analyses reported below were
obtained for XRF instrumentation that was optimized for the analytes Si and Ca in
a typical PC having a composition of 45% Ca and 10% Si. Due to the variability
of trace-element composition in PC, the detection limits for
Fe- and Sr-based analyses may deviate from the estimates
shown. Detailed comparisons of the PC SRMs are shown in Section 4.2.
For PC samples collected on polyvinyl chloride (PVC) membranes and transferred to
25-mm Ag membrane filters, the PC detection limits are shown below. These limits
are based on the analytical peaks (AP) for the major PC elements. The oxide
compositions shown were obtained from the NIST Certificates of Analysis.
|
![](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig02.gif) |
------ SRM 637 ------- |
![](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig02.gif) |
------ SRM 635 ------- |
![](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig02.gif) |
Counting |
AP
|
DL (µg PC)
|
% oxide
|
DL (µg PC)
|
% oxide
|
Time (s)
|
Si Ka Ca Ka |
11 13 |
23.1 66.0 |
16 17 |
18.4 59.8 |
200 200 |
The range of detection limits based on trace-element analyses of PC is very
susceptible to composition. The detection limits for PC from these trace elements are as
follows:
|
![](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig02.gif) |
------ SRM 637 ------- |
![](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig02.gif) |
------ SRM 635 ------- |
![](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig02.gif) |
Counting |
AP
|
DL (µg PC)
|
% oxide
|
DL (µg PC)
|
% oxide
|
Time (s)
|
Fe Ka Sr Ka |
95 210 |
2.61 0.21 |
160 640 |
1.80 0.09 |
1,000 1,000 |
Detection limits for mass absorption analyses are relatively unaffected by composition.
The detection limit for simple mass absorption (MA) analysis of PC using Ag L radiation from
Ag support membrane filters are as follows:
AP
|
![](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig02.gif) |
SRM 637 DL (µg PC)
|
![](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig02.gif) |
SRM 635 DL (µg PC)
|
![](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig02.gif) |
Counting Time (s)
|
MA |
180 |
190 |
200 |
1.3.2. Recovery, coefficients of variation, and overall error:
Combined results from air sampling at low humidity (SRM 635 and 637) and at 80% RH (SRM 637):
PC Mass range (mg)
0.6 to 7.7 |
n
26 |
R
1.001 |
CV
0.103 |
CVT
0.114 |
OE(%)
±22.9 |
1.3.3. Instrument response to the analyte:
The practical analytical range for the XRF analysis of PC elements on Ag membrane filters
extends from the detection limit up to about 4 mg. For thin-film analyses by
XRF, the upper end of the analytical range depends primarily upon self-absorption
of X rays within the sample. In the case of PC analyses, where the matrix is held constant,
the more energetic fluorescence lines have larger useful ranges. However, the same
sample is analyzed using all five lines, and thereby limits the maximum sample weight
to what can be practically analyzed by the low-energy lines. During the method
evaluation, examination of the PC calibration curves gave the following estimates of the
upper analytical limits:
Element
|
Energy (kV)
|
Mass PC(mg)
|
Comments
|
Si Ka MA Ca Ka Fe Ka Sr Ka |
1.740 2.984 3.691 6.403 14.164 |
5 5 5 10 15 |
Major element Ag membrane * Major element Trace element Trace element |
* Uses fluorescence from Ag membrane (L series X rays for Ag)
A more conservative estimate for the upper mass per analytical sample is 4 mg. Samples
exceeding 4 mg should be split into aliquots to be analyzed separately.
1.4. Advantages
1.4.1. The method provides for non-destructive analyses.
1.4.2. The sample preparation is compatible for both XRF and XRD analyses.
1.4.3. The method provides qualitative evidence of PC by comparing XRF and XRD spectral
patterns of air samples to those of reference material.
1.4.4. The method can provide additional qualitative information for a large number of
elements including any unexpected elements.
1.4.5. The method requires no sampling reagents and sample preparation is minimal.
1.4.6. Samples are screened gravimetrically in the field. Samples showing low exposures need
not be submitted for laboratory analysis.
1.5. Disadvantages
1.5.1. Samples with high sample weights (>4 mg) must be split into aliquots during analysis.
1.5.2. The method requires expensive instrumentation and support software.
1.5.3. The method requires the collection and analysis of pure PC bulk samples for
quantitative analysis and qualitative confirmation.
1.5.4. The method is not suitable for finished PC materials because comparable reference
materials are usually unavailable. Preliminary studies indicate that dry commercial
mixtures containing PC cannot be analyzed by this method. These include concrete,
sandcrete, fast-cure leak patching mix, and mortar mix.
1.5.5. The standards and samples prepared on Ag membrane filters should be stored prior to
analysis in a desiccator containing a drying agent in order to prevent sample hydration.
(See Sections 4.7. and 4.8.)
1.6. Toxicology
Information contained in this section is a synopsis of current knowledge of the physiological
effects of PC and is not intended to be used as a basis for OSHA policy.
Risks of exposure include eye, skin, and mucous membrane irritation, and may include more
severe respiratory effects, all of which constitute material health impairments (5.5.)
- Eye exposure (5.11.):
Suspensions of PC in vater, when splashed into the eye, cause smarting and corneal edema.
Aqueous suspensions are sufficiently alkaline to injure the corneal epithelium and conjuctiva.
- Skin exposure (5.11.):
Primary irritant dermatitis from repeated skin contact with PC includes symptoms of xerosis,
eczematous lesions with vesicles, erythema, fissures, and mild scaling. Portland cement
occasionally contains hexavalent chromium which may produce secondary contact sensitivity
in some individuals.
- Respiratory tract exposure (5.11.):
Symptoms include cough, expectoration, exertional dyspnea, wheezing, and chronic bronchitis.
Exposure can also cause chronic conjunctivitis, blepharitis, and ulcers of the nose.
Aside from irritation, PC is eventually eliminated from the tissue and is generally not
considered harmful when ingested (5.5.). However, PC added to grain has been
used as a rat poison; death is probably due to physical blockage of the gastrointestinal tract.
1.7. Sources of Exposure (5.11.)
Portland cement, hydraulic cement, CAS: 65997-15-1
Application
|
|
Source of exposure
|
Commercial PC |
Breaking-up and grinding clinker, mixing, packaging and shipping |
Commercial dry mixtures; concrete, mortars, grouts, and asbestos-cement |
Mixing and on-site uses for highway paving, domestic and commercial construction: structural support in mining industry |
Composites |
During manufacture of building blocks, bricks, stone, terrazzo, stucco, foamed concrete, and pre-cast items; as a moisture sealant on pre-cast blocks |
Portland cement should not be confused with refractory cements composed primarily of calcium aluminates.
2. Sampling
2.1. Safety Precautions
2.1.1. The sampling equipment should be attached to the worker in such a manner that it will
not interfere with work performance or safety.
2.1.2. All safety practices that apply to the work area being sampled should be followed.
2.2. Equipment
2.2.1. Air sampling equipment
- Low ash PVC membrane filter, 37-mm, 5-µm pore size
[part no. 625413, Mine Safety Appliances (MSA), Pittsburgh, PA or cat. no. P-503700,
Omega Specialty Instrument Co., Chelmsford, MAJ.
Note: During the preparation for analysis, the PVC membrane filter is dissolved in
tetrahydrofuran (THF). Certain acrylic copolymers added to PVC filters are insoluble in THF.
If the membrane filter composition is unknown, a laboratory test should be conducted with
THF to determine suitability before use.
- Cellulose back-up pads (support pads), (MSA, Pittsbutgh, PA).
- Polystyrene 37-mm diameter closed-face cassette, (3-section,
SKC part no. 225-3, SKC, Fullerton, CA).
- Gel bands (omega Specialty Instrument Co., Chelmsford, MA) for sealing cassettes.
- Sampling pump:
For personal samples, use a personal sampling pump that can be calibrated
to within ±5% of 1 L/min with the sampling device attached.
- Assorted flexible tubing.
- Stopwatch and bubble tube or meter for pump calibration.
- Analytical balance capable of 10 µg precision.
2.2.2. Bulk sampling equipment
Scintillation vials, 20-mL, part no. 74515 or 58515, (Kimble, Div. of Owens-Illinois
Inc., Toledo, OH) with polypropylene or Teflon cap liners. If possible, submit bulk samples in
these vials. Tin or other metal cap liners should not be used because chemical reaction with the sample can occur.
2.3. Sampling Technique
Note: Because PC composition is highly variable, a representative bulk sample of the
pure PC material must be submitted with total dust PC air samples in order to
define the particular PC composition to which the worker is exposed. Total dust PC air samples
can not be quantitatively analyzed without an appropriate pure bulk sample. If a pure bulk sample
can not be obtained, the industrial hygienist should sample for nuisance dust, and should not
submit the air samples for PC analysis.
Note: Respirable dust samples are normally not sent to the laboratory for PC analysis;
measure these gravimetrically in the field. If quartz is suspected, any air samples should be
submitted for quartz analysis. [See OSHA Method
ID-142
(5.7.) for further information.]
2.3.1. Air sample collection
Measure PC total dust air samples gravimetrically.
- Desiccate and then weigh the PVC filter before sampling.
- Place a cellulose backup pad in a cassette. Place the preweighed PVC filter on top of the
backup pad. If large loadings are expected and the membrane filter has a smooth and a rough
side, place the membrane filter in the cassette with the smooth side against the backup pad
and use a 3-section cassette to help produce a more adherent deposit.
Assemble the cassette.
- Attach tubing between the pump and a flow calibration cassette so that the air will be
drawn through the membrane filter. Do not place any tubing in front of the cassette.
- Calibrate each sampling pump to within ±5% of the recommended sampling rate of 1 L/min
with the calibration cassette attached in-line.
- Attach a prepared cassette to the calibrated sampling pump and place in the employee
breathing zone.
- If possible, take two half-shift samples at the recommended sampling rate.
- Place plastic end caps on each cassette after sampling.
- Carefully remove the filter from the cassette, desiccate, and weigh the PVC filter sample
to determine total dust exposures. Place each filter back in its cassette. Calculate the TWA
exposure for each employee using the sample weight(s) collected and air volume(s) used. If
the TWA exposure for any employee exceeds 10 mg/m3, submit the
sample(s) to the laboratory.
2.3.2. Bulk sample collection
Always collect a sample of powdered PC from the workplace.
Concrete mix or other PC mixtures with substantial additions of gravel, sand, gypsum, or lime
are generally not appropriate. Sampling these types of mixtures should be performed to
determine quartz content, pH, etc.
- Collect between 10 to 20 mL of dry homogeneous PC dust reference material
representative of the PC used in the workplace. Samples from bagged PC are
preferred. Accurate analytical results are dependent on a close match of the PC
bulk sample to the PC dust component of the air samples.
- Transfer the bulk material into a 20-mL scintillation vial, seal with a cap having an
inert plastic liner, and wrap the cap with vinyl or electrical tape.
2.3.3. Wipe sample collection
Wipe samples are not appropriate for this method.
2.4. Sample Shipment
2.4.1. On the OSHA 91, state the type of operation sampled. List the bulk samples and cross-reference these to the appropriate air sample(s).
2.4.2. Document the operation and indicate any known or suspected substances present in the area sampled.
2.4.3. Request Portland cement analysis.
2.4.4. Submit at least two blank samples with each set of air samples.
2.4.5. Attach an OSHA-21 seal around each bulk, air, and blank sample in such a way as to secure the end caps.
2.4.6. Ship air and blank samples to the laboratory with appropriate paperwork.
2.4.7. Ship bulk samples separately from air samples. They should be accompanied by
material safety data sheets if available. Check current shipping restrictions and ship to
the laboratory by the appropriate method.
3. Analysis
This method is optimized for the analysis of PC collected on PVC filters using an EDXRF system
for quantitation. A wavelength dispersive X-ray fluorescence (WDXRF) system may be used in
place of an EDXRF system.
The user must decide upon the applicability of available equipment and
software for this method.
As mentioned in Section 1., the XRD portion may be performed prior to the
XRF portion. Because the sequence of analysis is flexible, improved laboratory efficiency may
be obtained. Circumstances arise where subsequent analyses may be unnecessary:
- Subsequent XRD verification of PC is not needed if the preliminary XRF quantitation
indicates that exposures are less than the PEL. (Screening for quartz may still be advisable.)
- Subsequent XRF quantitation is not needed if the preliminary XRD analyses do not
qualitatively identify PC crystalline phases as present in the air samples.
3.1. Safety Precautions
3.1.1. Chemical
- Tetrahydrofuran has a low flash point, -14 °C (6 °F), and is extremely flammable.
Always use THF in a hood. THF is an ether which can form explosive peroxides upon exposure to
air; therefore, it should be stored in closed metal containers. Always use THF-resistant
gloves, a lab coat, and safety glasses when handling THF.
- Parlodion and isopentyl acetate are flammable and should be used in a hood.
- Handle reagents and bulk samples carefully. Use protective equipment such as:
gloves, laboratory coats, safety glasses, and an exhaust hood. Wear a fit-tested
respirator if necessary. Clean up spills immediately.
3.1.2. Radiation
- Follow established laboratory safety guidelines. Modern X-ray fluorescence
spectrometers and X-ray diffractometers have built-in safety devices
and interior to prevent X-ray exposure. WARNING: These devices should not
be adjusted removed, or overridden for any reason.
- X-ray operators should wear radiation monitors. These monitors consist of
badges and finger rings which are periodically analyzed to detect cumulative exposure to
low-level radiation.
- There should be a red or yellow warning light which, when lit, indicates that power
is supplied to the X-ray tube. The instrument may be checked for radiation leaks
using a sensitive radiation survey meter. Radiation leaks, if present, will be most
easily detected when the X-ray tube is operated at the highest power design
specification.
- Periodically, have safety mechanisms checked to determine satisfactory operation.
A sensitive, fixed position radiation alarm may be used as an area monitor;
however, damaging radiation exposures can occur in collimated beams that do not
intersect the monitor's probe.
- Avoid inserting fingers into the sample compartment; use forceps to change samples.
3.2. Equipment
3.2.1. X-ray fluorescence spectrometer
The specific equipment used in this evaluation is described in Section 4.
The spectrometer should be equipped with appropriate monitors, collimators, and secondary
targets. The spectrometer used to evaluate this method included the following items:
Lucite monitor
Tantalum collimator
Silver secondary target with silver filter
NaCl secondary target (see Section 3.6.3. step 3.)
3.2.2. X-ray diffractometer
The specific equipment used in the evaluation is described in Section 4.
The automated powder diffractometer (APD) should be equipped with an output device that can
provide hardcopies of scans. Other useful features include:
Spinning sample holders
Support software for:
Storing, recalling, and comparing spectrum files
Locating peaks and determining peak intensity
Profile fitting
Powder diffraction file library
3.2.3. The following equipment can be used:
- Standard and sample preparation
- Sieve, nylon, 41-µm (Spectra/Mesh N sieve, Cat. no. 08-670-202,
Fisher Scientific, Springfield, NJ) or (Cat. no. 146502, Spectrum Medical Industries, Inc.,
Los Angeles, CA). A mini-sieve may be constructed by sandwiching the nylon mesh
between the two spacer rings of a four-piece 37-mm air sampling
cassette. Similar non-contaminating sieves may be used.
- Low ash PVC membrane filters, 37-mm, 5-µm pore size
[part no. 625413, Mine Safety Appliances (MSA), Pittsburgh, PA or cat. no. P-503700,
Omega Specialty Instrument Co., Chelmsford, MA].
- Analytical balance capable of 10-µg precision.
- Centrifuge tubes, round bottom, 40-mL (Pyrex 8260).
- Gloves, THF-resistant [such as latex gloves (Cat. no. 8852, American
Pharmaseal Lab., Glendale, CA)].
- Forceps.
- Silver membrane filters: 25-mm diameter, 0.45-µm pore size (Cat. no. FM25-0.45,
Osmonics, Inc., Minnetonka, MN).
- Ultrasonic bath.
- Filtration apparatus: 25-mm (Filter Holder Hydrosol Manifold, cat. no. XX25 047 00,
filtering clamps, cat. no. XX10 025 03, fritted glass bases with stoppers, cat. no.
XX10 025 02, and glass funnels, cat. no. XX10 025 11, Millipore Corp., Bedford, MA).
- Liquid nitrogen cold-trap system for THF collection (dewar, polypropylene
vacuum flask, liquid nitrogen, etc.).
- Eyedropper and glass plate.
- Hot plate, intrinsically safe (Model HP-11515B, Sybron/Thermolyne, Dubuque, IA).
- Teflon sheet, 0.3- to 1-mm thick (cut to fit top of hot plate).
- Plastic petri dishes (Product no. 7242, Gelman Sciences, Ann Arbor, MI).
- Vacuum desiccator with anhydrite (CaSo4) or other drying agent.
- Vacuum system.
- Accessories for XRF analyses
- Laboratory press, 12-ton (Cat. no. A14-100, Kevex, San Carlos, CA.).
- Pellet die set for preparing Cl secondary target, 13-mm diameter (Cat. no.
A10-401, Kevex).
- Powder secondary target holders, 13-mm diameter (Cat. no. A00-205, Kevex).
- Sample holders for 25-mm diameter Ag membrane filters (Cat. no. A00-213,
Kevex). Note: These holders may require light machining in order to center the Ag membrane
filter over the most sensitive spot.
- Pellet die set for preparing MCA energy calibration sample, 31-mm diameter
(Cat. no. AI0-403, Kevex). Note: The 13-mm diameter die set may be
used instead.
- Sample holder for 31-mm diameter MCA energy calibration sample (Cat. no.
A00-214, Kevex). Note: If a 13-mm diameter pellet is used,
substitute a 13-mm diameter sample holder (Cat. no. A00-212, Kevex).
- Radiation safety monitor (S.E. International Instrumentation Model Radiation Alert
Monitor 4, S.E. International Instrumentation Division, Summertown, TN).
- Accessories for XRD analyses
- Sample holders for 25-mm diameter Ag membrane filters (Model no. PW1813/26, Philips
Electronics Instruments Co., Mahwah, NJ).
- Radiation safety monitor, see item [b)7)] above.
3.3. Reagents (use at least reagent grade chemicals)
3.3.1. XRF MCA energy calibration
- Titanium dioxide
- Zinc oxide
- Yttrium oxide
- Boric acid (H3BO3)
3.3.2. Sample preparation
- Tetrahydrofuran (dry).
- Parlodion (Pyroxylin).
- Isopentyl (Isoamyl) acetate.
- Parlodion in isopentyl acetate, 1.5% (w/v):
Dissolve 1.5 g of parlodion in isopentyl acetate and dilute to 100 mL with isopentyl acetate.
3.3.3. XRF secondary target
- Sodium chloride
- Pellet binder (Chemplex Liquid Binder, Cat. no. D12-400, Kevex).
3.4. Instrument Calibration
3.4.1. XRF calibrations
Use appropriate materials and manufacturer recommendations when calibrating specific
Instrumentation and software. Examples of the calibrations performed on specific EDXRF
equipment in Section 4. are given in the Standard Operating Procedure
(5.12.).
- If one is not already available, prepare an appropriate standard(s) for MCA energy
calibration of the EDXRF spectrometer. For the instrumentation described in Section 4.
prepare a sample consisting of a H3BO3 powder pellet containing 5 to
10% of an equimol mixture of the oxides of Ti, Zn, and Y. Place this sample in a sample holder, and then place in the EDXRF spectrometer.
- Perform an MCA energy calibration.
- Use excitation conditions for the Ag secondary target as described in Section 3.6.3. step 3b.
Use an analysis time adequate for 2,000 count peak height on the shortest calibration peak.
- Make a two-point MCA energy calibration using the Zn and Y Ka
lines (8.631 and 14.933 kV).
- Determine the peak-width at half-maximum for calibrating the peak
profile-fitting (deconvolution) software. This calibration is not routinely needed;
it is typically performed when the spectrometer is installed or when indicated by preventative
maintenance checks.
3.4.2. XRD calibrations
- Hardware 2q calibration:
This type of instrument calibration should be performed only by trained personnel.
The calibration should be checked periodically using a stable reference standard
consisting of polycrystalline quartz (Arkansas stone) or polycrystalline silicon.
- Software 2q calibration:
Sample displacement errors may result in a systematic bias in 2q
peak locations. The Ag membrane filter may be used as an internal standard to correct for the
sample displacement errors of thin samples. Scan either the primary or secondary
Ag diffraction peaks at 38.15° and 44.33° 2q,
respectively. Offset the 2q values for the remainder of the scan for
each sample by the same amount that the observed Ag line was offset from its theoretical
2q value. For example, if the secondary Ag line that should occur at
44.33° 2q is found at 44.45°, correct all observed lines
by subtracting 0.12°.
3.5. Sample Preparation
Note: The PC standards, air samples, and blanks should be prepared using the same lot of
silver membrane filters in order to reduce variability in mass absorption analyses.
3.5.1. Air samples and blanks
- Note which air sample weights are greater than 4.0 mg.
- Examine the filter and backup pad to determine if any breakthrough to the backup
pad has occurred. If there is significant breakthrough, the sample is either not
analyzed or results are reported with a disclaimer (see Section 3.10.3.
for reporting results).
- Assemble the filtering apparatus and liquid nitrogen cold trap. Connect the cold
trap to the filtering apparatus to collect the waste THF. Any waste vapors should
not enter the vacuum pump.
- Center a Ag membrane filter on the fritted-glass base of the filtering apparatus.
Also center the glass chimney on top of the base and secure it with a clamp.
- Carefully transfer the respirable air sample (PVC filter) from the cassette to a
round-bottom 40-mL centrifuge tube.
- Add 10 mL of THF to each centrifuge tube to dissolve the filter and suspend the
sample. Use an additional 10 mL for air samples greater than 4.0 mg. Sonicate
the sample suspension for 15 min.
- With the vacuum turned off, place 2 to 5 mL of THF in the chimney of the
previously assembled vacuum filtering apparatus.
- For samples <4.0 mg: Quantitatively transfer the suspension with rinses of THF
to the glass chimney of the vacuum filtering apparatus. The total volume in the
chimney should not exceed 20 mL.
For samples >4.0 mg: Divide up suspensions by delivering appropriate aliquots
of the suspension to additional glass chimneys. Each aliquot should contain less
than 4 mg of sample particulate.
- Apply vacuum to the filtering apparatus, drawing the THF through it. This should
result in a thin, even layered deposition of the sample on the Ag membrane filter.
Do not rinse the chimney after the material has been deposited on the membrane
filter. Rinsing can disturb the thin layer deposition just created. Vacuum should
be applied for sufficient time to dry the membrane filter.
- Carefully disassemble the chimney and clamp. Remove the Ag membrane filter
from the firitted-glass base using forceps. Place 2 drops of 1.5% parlodion
solution on a glass plate. Fix the dust to the membrane filter by placing the
bottom side of the membrane filter in the parlodion solution. By capillary action,
the membrane filter draws the parlodion solution to the analyte surface. Place a Teflon
sheet on top of an intrinsically-safe hot plate which is set at the lowest
setting. Place the Ag membrane filter on top of this heated Teflon sheet.
- When dry, place the fixed sample in a labeled Petri dish.
- Store Petri dishes holding the prepared samples and standards in a desiccator
containing a drying agent.
3.5.2. Standard preparation
- Do not grind the bulk sample. Size a representative portion of the bulk sample,
using a 41-µm sieve. This results in a sample particle size of less than
41 µm (fines). Place the fines in a scintillation vial.
- Re-sieve the material remaining on the sieve to obtain additional fines. Add the
fines to the material obtained in step 1. Repeat this step until no additional fines
are obtained. Cap the vial.
- Rotate and shake the vial to mix the combined PC fines thoroughly. This is the PC
stock material from which standards are prepared.
- Weigh out six different-size aliquots of PC stock material in the range
of 0.5 to 6 mg on PVC filters. Useful nominal weights are 0.5, 1.0, 2.0, 3.5, 5.0, and
6.0 mg. Carefully place each PVC filter containing the weighed PC stock material
in separate, labeled, round-bottom centrifuge tubes. Standard amounts are selected
to bracket the expected analytical range of the air samples. The higher standards
(>3.5 mg) are useful to determine the analytical range for particular PCs.
- Place a blank PVC filter in a labeled round-bottom centrifuge tube.
Note: This blank and the blanks supplied with the air sample
set are used to check for contamination of sampling media and as reagent blank standards in
the calibration. They may also be used to estimate the analytical detection
limit for a particular PC (See Section 4.2.).
- Prepare the six standards and blank as air samples using steps 5 through 12 in
Section 3.5.1. DO NOT split standards greater than
4.0 mg; they are used to calibrate above 4.0 mg.
- Inspect the deposit for uniformity; clumping indicates that insufficient sonication
was used. Remake the standard if a significant amount of clumping occurs.
- Place the THF waste in an explosion-resistant metal container and dispose
appropriately.
3.6. Analysis - XRF
3.6.1. Assemble sample holders for the Ag membrane filters on a clean dust-free
surface. Load each sample in a sample holder. Precise sample positioning is critical for
reproducible instrument response and reliable intensity data.
3.6.2. The most sensitive location for the sample in the XRF is determined by trial-and-error
using copper peak intensities from a small ring of fine copper wire resting on a
polypropylene film. Mark tie location of the ring center with a felt-tipped pen,
and reposition the sample on the polypropylene film until a maximum signal is reached.
Sample holders can be customized to center the Ag membrane filters at the most sensitive spot.
Note: Si and Ca Ka lines are low energy
X rays; sample holders prepared using polypropylene film will give reduced sensitivity for these
lines. For this reason, sample holders without any support film are preferred.
3.6.3. Analytical conditions for quantitative XRF
(For typical analytical sensitivities see Section 4.3.) Use X-ray
excitation conditions appropriate for the system and software. If calculations are not performed
immediately after each scan, the spectra should be saved for later use. Conditions selected for
analysis should match those used during calibration. For the spectrometer, specified in
Section 4., the following conditions are recommended (Refer to Reference 5.12.
for additional details.):
- Use a Ta collimator.
- Use a Lucite monitor so calibration and analytical data may be collected and used over a
period exceeding one day. Correct the count data for analyses performed on subsequent days to
comparable first-day intensities by using a ratio of monitor data obtained on the
different days. Optimize the spectrometer to obtain a maximum counting rate which does not
exceed a 50% deadtime using the Lucite monitor. Samples normally will give lower count rates
than the monitor.
- Two different instrumental conditions are used to obtain data for the monitor, samples, blanks, and standards:
- Si, Ca, and MA
If a Cl secondary target is unavailable, prepare one by pressing a 13-mm pellet at
8 tons under vacuum from a mixture of 0.58 g powdered NaCl and 7 drops of liquid binder.
Glue the pellet into a secondary target holder and install it in the secondary target wheel.
Use the Cl secondary target (as NaCl) to quantitatively analyze PC for Si, Ca, and the sample
mass absorption of the Ag L lines from the fluorescing Ag membrane filter. Chlorine X rays
from the secondary target efficiently fluoresce Si. Sufficient white (broad
non-monochromatic) X-ray intensity is available from the NaCl to
excite Ca and Ag.
Analyze Si, Ca, and MA samples as follows:
- Operate the primary Rh target at 15 kV and 3.3 mA.
- Samples are analyzed with the MCA set to the 10 kV energy scale.
- Analyze for 200 s counting time
- Use a vacuum.
- Fe and Sr
Use a Ag secondary target for the quantitative analysis of the trace elements Fe and Sr.
Analyze Fe and Sr samples as follows:
- Operate the primary Rh target at 35 kV and 0.5 mA.
- Analyze samples with the MCA set to the 20 kV energy scale.
- Analyze for 1,000 s counting time.
- Analyze samples in air.
3.7. Analysis - XRD
Note: Do not store any Ag membrane filter samples on aluminum sample holders.
(See Section 4.7. for further details.)
3.7.1. Use X-ray power levels appropriate for the target and hardware in use.
For the instrumentation described in Section 4., the following conditions are recommended:
- Power the tube to 40 kV and 40 mA.
- Use a sample spinner.
- For each sample, perform scans consisting of 0.02° 2q
steps with 10-s duration. For example:
Scan (2q)
|
PC peaks (2q)
|
27 to 36° 50 to 54° |
![](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig03.gif) |
29.5° 32.7° 34.4° 51.8° |
Either multiple narrow-angle scans or a single wide-angle scan can be used.
3.7.2. Desirable XRD analyte sensitivities
(For typical analytical sensitivities see Section 4.3.2.) A minimum
desirable sensitivity for integrated peak areas should approach 10 counts/µg (10,000 counts/mg).
3.7.3. Assessment of the presence of PC
An automated pattern search of a powder diffraction library such as the Joint
Committee on Powder Diffraction Standards (JCPDS) powder diffraction file of the
International Centre for Diffraction Data may be useful in identifying other constituents.
3.8. Interferences
3.8.1. Positive XRF interferences include background signals arising from either:
- instrument artifacts
- electronics
- collimators
- target and filter fluorescence
- target and filter Compton and Rayleigh scatter peaks
- escape peaks
- sum peaks
- sample displacement towards the secondary target and/or detector
- or -
- sample matrix interferences
- overlapping sets of M, L, and K spectral lines (MLK lines from elements other than those
of interest)
- matrix specific enhancement such as the additional florescence of Ca resulting from
excitation by Ti fluorescing in a sample
The effect of most interferences can be minimized or resolved. For example, a potassium
Kb line that overlaps the calcium
Ka line can be resolved through
profile-fitting. Interferences arising from sample preparation materials may be
resolved using blanks. Sum and escape peaks can be resolved by software. Alternate analytical
lines are often available to resolve interferences. (Note: Lines from the Ta collimator can
potentially interfere with the analysis of Si.)
3.8.2. XRD interferences
Other diffraction peaks may be present in the sample that may present positive interferences:
Interferent
|
|
Peaks (2q)
|
Ag
Gypsum (CaSO4 · 2H2O)
Anhydrite (CaSO4) |
28.0, 32.2°
29.2, 31.2, 33.5, 34.7, 50.5, 51.3°
28.0, 31.5, 32.2, 52.5° |
3.9. Calculations
3.9.1. XRF result calculations
The sequence of steps in calculating results from the XRF data depends on software
requirements. Alternate sequences may be necessary when using different software.
- Perform escape peak corrections.
- Perform sum peak corrections, if available.
- Perform background modeling and subtraction.
- Identify the elements and interferences present using software tools provided with
the XRF system in use.
- Decnvolute (profile-fit) the identified elements to obtain integrated (area) counts for
the analytical peaks.
- Check for residual peaks, and repeat steps 4 and 5 until all potentially interfering
peaks are accounted for.
- If the analyses are performed over a period of more than one day, use monitor data
to correct for changes in X-ray tube output.
- Calculate the mean blank Ag L peak intensity (Iblank) for the field and reagent blanks
(Section 3.5.2. step 5). Count data for three blanks are averaged in
order to provide a more accurate estimate of Iblank.
- Calculate the sample mass-absorption Ag L counts for all air samples, blanks,
and standards by subtracting the net Ag L peak intensity of each from the mean blank
Ag L peak intensity (i.e., Iblank - Isample).
Note: The MA calculation is not the same as blank subtraction; the order of
subtraction is reversed because the Ag L peak intensity of the blank is greater than
that of the samples. Another consequence of MA analysis is that blanks have a
larger counting error than other samples; therefore, negative net counts are
possible for blanks or lightly loaded samples.
- For each of the five analyses (Si, Ca, MA, Fe, and Sr), tabulate the data for the
theoretical µg PC and integrated peak areas for the blanks and standards. A
typical example follows:
PC
|
Si
|
Ca
|
MA
|
Fe
|
Sr
|
(µg)
| Counts
|
0 · · · 6,000 |
0 · · · 21,611 |
0 · · · 17,283 |
108 · · · 8,419 |
0 · · · 4,248 |
0 · · · 1,824 |
- Construct a concentration-response calibration curve for each of the five
different analyte elements. (For further suggestions and examples see Appendix A.)
- Use the curves from step 11 to calculate the µg PC in each air sample for each analyte element.
Negative weights are possible for non-detected samples near the intercept of the
calibration curve. Round negative µg PC results to zero for use in subsequent calculations.
- For each analyte element, sum together the µg PC determined for aliquots of split samples.
If blanks supplied with the sample set are contaminated, subtract the µg PC contamination
for the specific element from each sample result in the set.
- For each sample, rank the µg results from the five analyses. For example, sample A4 gave the
following results:
Si
|
Ca
|
MA
|
Fe
|
Sr
|
(µg)
|
1,958 | 1,842 | 2,056 | 2,020 | 1,868 |
These results are ranked as follows: |
Low
|
| Median
|
| High
|
1,842 | 1,868 | 1,958 | 2,020 | 2,056 |
- Select the median (middle) value from the five ranked PC results. In the example given in
step 14 above, the result 1,958 µg is selected. (The actual mass of PC aerosol spiked on
PVC filter A4 was 1,910 µg. Additional examples of rankings and recoveries are given in
Tables 1 and 2. of Section 4.4.2.)
For air samples, calculate the PC exposure (mg/m3) by dividing the
median value (µg) by the sample air volume (L). If sample A4 had resulted from sampling a
total air volume of 230 L, it would represent an exposure of 1,958 µg / 230 L = 8.51
mg/m3. Exposure results for PC are not final until PC is qualitatively confirmed.
3.9.2. XRD calculations
Deconvolute the XRD peak intensities and compare the diffraction patterns of standards with air
samples having similar weights. X-ray diffraction peak intensities can be very
sensitive to preferred orientations and particle-size distributions, and
intensities may not always be comparable between samples and standards.
3.10. Reporting Results
Both XRD and XRF data are considered before reporting the results to the IH. Interpretation of
XRF or XRD results requires experience and analyst interaction.
3.10.1. XRF results
- Compare the experimental and theoretical XRF line energies to qualitatively confirm the
presence of analyte elements., They should compare within ±0.01 kV or be comparable within the
range of variability exhibited by standards. When instrument resolution and sensitivity permit,
seek qualitative confirmation on secondary analyte lines.
Good agreement of the middle three ranked results (Section 3.9.1. step 14)
provides quantitative XRF verification. Too wide a spread may indicate significant contamination
by substances other than PC.
- Compare the result by this method (Section 3.9.1. step 15) with the
gravimetric result measured by the industrial hygienist.
3.10.2. XRD results
- Match the 2 peak locations of air samples to standards in order to establish a qualitative
XRD "fingerprint" of PC components. Peak locations of air samples are expected to be within
±0.1° 2q) of the peak locations exhibited by standards.
Note: Due to ion exchange, the peak locations for the major PC phases often
differ from data obtained from pure phases or patterns listed in the literature.
After PC is identified by XRD, report the result determined in Section 3.9.1.
- The XRD intensities should be comparable for standards and air samples of equivalent weight
having similar particle-size distributions.
3.10.3. Disclaimers
Particulate present on the backup pad constitutes some sample loss. Occasionally this
may be seen and can be due to a poor cassette seal on the filter, improper positioning of
the filter in the cassette, or poor quality control of the filter and/or cassette. If this type
of contamination occurs, relay a note to the compliance officer indicating that some of
the sampled material was found on the backup pad and the reported value may be lower
than the actual exposure.
4. Validation-Backup Data
The EDXRF spectrometer used in the validation was a Kevex 770/8000 Delta system (Kevex
Instruments Inc., San Carlos, CA) consisting of: Kevex 770 X-ray generator, its
associated satellite box, vacuum system, helium flush system, firmware-based
8000 keyboard console, computer monitor, Digital Equipment Corporation (DEC) 11/73 computer,
graphics memory, Kevex spectrum analyzer, and Toolbox II software. A wavelength dispersive
X-ray fluorescence (WDXRF) system may be used in place of an EDXRF system.
The APD used in the validation was an APD 1800 (Philips Electronics Inc., Mahwah, NJ). It
included an X-ray generator, long fine-focus copper target
X-ray tube, proportional gas counter detector, pulse-height analyzer,
graphite monochromator, 2q compensating slit, 1° receiving slit,
sample spinner, sample changer, recirculating cooling system for the X-ray tube,
and associated software (Version 3.5) using the laboratory DEC VAX 750 computer.
The backup data validation contains the following protocol:
4.1. Experimental considerations
4.2. Detection limit estimates
4.3. Analyte sensitivities
4.4. Analytical data
4.5. Recovery and coefficients of variation
4.6. Overall error
4.7. Storage tests and 100% RH tests of prepared samples
4.8. Conclusions
4.1. Experimental Considerations
4.1.1. A 41-µm nylon sieve is used in the method (Section 4.4.1.). This effectively excludes particles larger than 41
µm from the analysis. The selection of the 41-µm nylon sieve for the
preparation of the PC bulk reference materials is based on the following considerations and experiments:
- Nylon is non-contaminating.
- Portland cement dust is reported to range in size from 0.2 to 100 µm (5.1.).
- Most of the major tricalcium silicate (alite) phases are in the range of 15 to 40 µm
(5.1.).
- There is a significant decrease in XRF sensitivity to the major phase elements Si and Ca
for larger particles. Material passing through 400 or 325 mesh sieve (37 to 44 µm) has been
considered generally applicable for XRF powder analysis of elements as light as aluminum
(5.14.).
- In a preliminary study, five different Portland cement materials were sized using the
41-µm nylon sieve. In all cases, most of the material passed through the sieve:
PC
|
% <41 µm
|
SRM 635 SRM 636 SRM 637 SRM 1881 Wülfrather SRM 1880 |
77.6% 83.7% 96.6% 95.1% 94.3% ~97.% |
Four SRMs (from NIST) and Wülfrather PC material (from SA) were evaluated.
The SRM 1880 was not sized in this study. However, the NIST documentation describing both SRM
1880 and SRM 1881 indicates maximum diameters of approximately 43 µm and 50 µm,
respectively. A graphic representation of particle distributions (in reference
5.2.) show that SRM 1880 has a much smaller percent of particles above
41 µm than does SRM 1881.
- Gravel, sand, and other large particles are often added to commercial mixtures to
decrease the void space in the finished material. Other PC-related commercial
mixtures were sized with the 41-µm nylon sieve. Only a small fraction of each
passed through the sieve:
Material
|
% <41 µm
|
Water patch Sandcrete Mortar mix Concrete mix |
36.7% 31.4% 22.4% 15.0% |
The sample preparation procedure in this method avoids many potential
interferences from commercial mixtures by not grinding the bulk reference material.
- The respirable range is 0.5 to 10 µm. Particles larger than 10 µm generally are
stopped in the nasal passages. The 41-µm limit is set well above 10 µm
in order to support the total dust PEL (10 mg/m3).
- Particles <41 µm include all respirable PC dust and would include most total
PC dust. It can be shown that PC particles >41 µm rapidly settle out of the air
leaving only the finer particles (See Appendix C).
4.1.2. Selection of representative SRM materials for sample spiking and detection limit determinations:
Certificates of analysis and preliminary experiments were used to determine which of four
different SRM materials would be most suitable to evaluate. The table below summarizes the factors considered.
| ------------------ % of Component -------------------------- |
Attribute
|
SRM 635
|
SRM 636
|
SRM 637
|
SRM 1881
|
SiO2 CaO
Fe2O3
SrO <41 µm |
18.4 59.8 2.61 0.21 77.6 |
23.2 63.5 1.61 0.04 83.7 |
23.1 66.0 1.80 0.09 96.6 |
22.2 58.7 4.68 0.11 95.1 |
| ------------------ Calibration Curve -------------------------- |
Attribute
|
SRM 635
|
SRM 636
|
SRM 637
|
SRM 1881
|
Scatter Linearity | (most) (poor) | | (least) (good) |
For calibration curves, standards were prepared from PC SRM stock material as described in
Section 3. SRMs 635 and 637 were selected because they exemplified the worst
and best cases overall and were the best compromise in representing the widest composition.
4.1.3. The selection of experimental conditions and appropriate SRM for study of humidity
effects on samples was based on the following factors:
- The hydration process of poured PC stops when the RH is below 80% (5.1.).
- Portland cement chemically combines with water. The amount of water normally retained after
strong drying ranges from 20 to 25% (5.1.). Samples of the sieved SRMs
were weighed and then exposed to air at 100% RH for 48 h at room temperature. They were
reweighed, placed in a vacuum desiccator, and dried to constant weight. They gave the following
irreversible weight gains:
SRM 635
20.8% |
SRM 637
23.6% |
The SRM 637 was selected to perform the humidity study because it had the higher irreversible weight gain.
4.2. Detection Limit Estimates
4.2.1. Experimental design
The following approach was used to estimate detection limits for the two PC SRMs (SRM 635 and SRM 637):
- X-ray tube currents were set to values that gave a maximum of 50% dead time
on a Lucite monitor. Sample analysis time was 200 s for the MA analysis and for the analysis
of the elements Si and Ca; and 1,000 s for the trace elements Fe and Sr. The same analysis time
was used for both blanks and samples.
- The approach used to calculate detection limits is attributed to Birks (5.15.)
and is given in Bertin (5.14.). [Note: Although widely used as an estimate
of the qualitative detection limit, this theoretical approach may not be appropriate for
samples containing significant interferences. The PC DL estimates calculated may be lower than
would be obtained experimentally by other approaches. For example, at low jig levels, dust may
penetrate into the Ag membrane filter with resulting shadowing and reduced sensitivity.]
The following equation (based on Poisson counting statistics) was used to estimate µg
detection limits:
Where:
B = blank background counts
S = sensitivity (analyte counts/µg PC)
Portland cement detection limit estimates were determined for all five analyses
(Si Ka, Ca Ka, MA, Fe Ka
and Sr Ka). The sensitivity for each analysis can vary depending on
sample composition. Standards (2-mg) of the two SRMs were used to obtain the net
counts for each analyte. These spectra were background-modeled and
background-subtracted prior to profile-fitting each analyte peak.
Except in the case of MA analyses, the net counts for the fit peak and the analyte counts were
the same. The analyte counts data used for the MA analyses were obtained by subtracting the net
Ag counts of each standard from the mean net profile-fit Ag counts for the blanks.
Energy spans used in profile-fitting the standards were comparable to those
used to integrate the background of the blanks.
In profile-fitting, the peak intensity affects the selection of the integration limits. The
software generally selects narrower integration limits for smaller peaks. Using such narrow
limits would give unrealistically low estimates for the variation in background counts.
Therefore, the integration limits used to determine the background counts for blanks were based
on the profile-fit integration limits used in the analysis of a 3-mg
SRM 637 sample exposed to 80% RH for 4 h. (This sample had been used in the humidity study and
is listed as sample T8 in Table 1.)
4.2.2. Results
The data for blank samples T1, T2, and B11 were used to calculate mean blank background count data:
|
Integration |
------------ Blank background counts ------------ |
Line
|
kV limits
|
T1
|
T2
|
B11
|
Mean
|
(Mean)½
|
Si Ka
Ca Ka
*MA
Fe Ka
Sr Ka |
1.560 to 1.940
3.500 to 3.880
2.850 to 3.120
6.180 to 6.620
13.860 to 14.400 |
442 368 8,056 1,231 1,695 |
300 279 7,974 1,202 1,667 |
354 293 7,908 **(2,018) 1,528 |
365 313 7,979 1,216 1,630 |
19.1 17.7 89.3 34.9 40.4 |
* | The MA data are derived primarily from the Ag L peak and are not
background counts; however, the MA blank data are used in the analysis to
blank-correct the mass-absorption analytical data in a manner
comparable to blank subtraction. |
** | Blank sample B11 was contaminated with Fe as evidenced by the presence of a
significant Fe Ka peak (~800 counts above background.) The Fe
contaminant may have come from the forceps used in preparing the sample. This outlier was not
used in determining the mean. |
The XRF DLs derived from these data are compared and listed with sensitivities in
Section 4.3.1.
The PC DLs for the Fe and Sr analyses can vary considerably because the amounts of these trace
elements are highly variable. Because the fluorescence X rays of these elements are penetrating,
particle-size effects are not expected to significantly complicate matters; the PC
DL of these elements are expected to be a linear function of the composition of PCs encountered
in the workplace.
The PC DLs for the Si and Ca major-element compositions are less variable because
PC SiO2 and CaO compositions are expected to be in the range of the
two SRMs studied. However, the PC DLs of these elements are not expected to be simple linear
functions of composition because the fluorescence X rays of these elements (particularly Si)
are less penetrating than those of Fe and Sr and are therefore more prone to significant
particle-size effects.
The PC DL tends to be large for the MA analyses because the counting error is greater
for large peaks than for the low backgrounds. Matrix composition does not appreciably affect
the sensitivity for the MA analyses; therefore the PC DL for the MA analyses should not vary
significantly between different PCs.
4.3. Analyte Sensitivities
4.3.1. XRF PC sensitivities
Analytical sensitivity (counts/µg PC) is matrix dependent. For the elements Fe and Sr,
which produce relatively penetrating X rays, the sensitivities are roughly proportional to the
concentration of analyte element; materials with smaller amounts of analyte element tend to
give lower sensitivities. The Fe and Sr trace-element composition of PC varies
considerably from one PC to another resulting in different sensitivities for different PCs.
Although the Si and Ca composition of PC is not as variable as that of Sr and Fe, the X rays
from Si and Ca are not as penetrating as those of Fe and Sr; therefore PC analyses using the Si
and Ca X rays are more susceptible to particle-size effects. In homogeneous
materials, large particles generally yield sensitivities that are lower than those of small particles.
The analysis least affected by the PC composition is that based on mass absorption of the
Ag L lines from the Ag membrane filter support.
For the analytical conditions described in Section 3.6., the following
analyte sensitivities were found:
|
---- Counts/µg PC --- |
|
--------- Composition --------- |
Line
|
SRM 635
|
SRM 637
|
SRM 635
|
SRM 637
|
Component
|
Si Ka
Ca Ka MA
Fe Ka
Sr Ka |
3.6 3.2 1.4 1.1 0.57 |
5.4 4.0 1.5 0.67 0.19 |
18.4% 59.8% --- 2.61% 0.21% |
23.1% 66.0% --- 1.80% 0.09% |
SiO2 CaO mass Fe2O3 SrO |
As indicated in the equation in Section 4.2., DL and sensitivity are related. Using the
analytical conditions described in Section 3.6., the two SRMs in the evaluation gave the
following correspondences between sensitivities and DLs:
|
----- SRM 635 ----- |
|
----- SRM 637 ----- |
Line
|
Counts/µg
|
DL (µg)
|
Counts/µg
|
DL (µg)
|
Si Ka | 3.6 | 16 | 5.4 | 11 |
Ca Ka | 3.2 | 17 | 4.0 | 13 |
MA | 1.4 | 190 | 1.5 | 180 |
Fe Ka | 1.1 | 95 | 0.67 | 160 |
Sr Ka | 0.57 | 210 | 0.19 | 640 |
The data show that a low sensitivity translates as a high detection limit.
4.3.2. XRD sensitivities
Using the analytical conditions described in Section 3.7., the following
are approximate sensitivity ranges observed for five different PCs (Wülfrather and SRMs
635, 636, 637, and 1881):
Peak location (Degrees 2q)
|
Integrated peak sensitivity (counts/µg PC)
|
29.5 32.7 34.4 51.8 |
23 to 79 28 to 76 42 to 80 15 to 55 |
4.4. Analytical Data
Due to the lack of a sophisticated aerosol generation/particle sizing system and the high cost
of NIST SRM materials, certain economies had to be undertaken for the collection of PC in air
during the evaluation.
4.4.1. Experimental procedure - spiked samples
- In the industrial environment, only a small fraction of the PC in use would become
suspended in the air. The analytical portion of this method requires that the standards be
prepared from exhaustively sieved PC bulk. For the purpose of this experiment, the SRMs used in
spiking samples were not exhaustively sieved in order to produce a variability in
particulate sizes and matrix similar to what might occur in industrial hygiene sampling.
Simulated air samples were prepared directly from SRM material as received from NIST;
aliquots of the unsieved material were briefly shaken from a 41-µm nylon
sieve into an air stream and deposited onto PVC filters. Only a small fraction of the
material passed through the sieve during the 1 to 2 min of shaking. The following diagram
shows the device used in preparing the simulated air samples:
Simulated "Air" Sample Preparation
Note: The diagram shown above describes the apparatus used in spiking validation
samples with PC aerosol. This diagram is not intended to represent proper field sampling.
- Sample collection in dry air was evaluated by collecting the suspended dust SRMs in
laboratory air on tared PVC membrane filters using the device shown above (2-min
sampling, 2 L/min, 30 to 40% RH). Sampling was followed by weighing to determine the net weight
of PC collected. These samples are referred to as "Dry" in the tables below.
- Any affect from humid air was evaluated by first collecting suspended dust samples of SRM
637 in dry air (as above). Next, humid air was drawn through the samples (4-h
exposure, 1 L/min, 80% RH). This was followed by reweighing. The net weight gain during
exposure to humid air was 0.2%. These samples are referred to as "80% RH" in the tables below.
- As stated above, only a small portion of each aliquot of the NIST SRMs was actually
delivered to each PVC filter. The proportions delivered to the filters are listed below:
SRM 635 (Dry)
3.5% to 10.4% |
SRM 637 (Dry)
6.7% to 21.5% |
SRM 637 (80% RH)
7.0% to 17.2% |
4.4.2. Analytical results
Samples were prepared and then analyzed by XRF following the procedure in Section 3.
- The tables which follow contain ranked lists of PC weights found using analyses based on
the five analytes. The theoretical (gravimetric) weight of PC for each sample is also shown.
- The recovery (R) is based on the reported median and is calculated from Found/Theoretical.
The coefficient of variation (CV) is shown for each experimental group. Additional samples
were analyzed along with the standards and simulated air samples in order to provide a check
on reproducibility and to evaluate storage stability. These additional samples are referred to
as quality assurance samples.
- In assessing the agreement between theory and experiment, the symbol
"
"
locates the position of the theoretical weight in the ranked lists. When the theoretical weight
is the same as one of the found weights, the
" "
replaces the decimal point (e.g., the "high" value for sample All in Table 1).
The analyses that gave results that bracket the theoretical weight are indicated in the column
labeled "[Ana]".
Table 1 SRM 637 - Recoveries
SRM 637 Dry Air Spiked Samples: |
Air |
Theor. |
| |
------------------ µg PC Found ----------------- |
| |
Sample |
Wt.(µg) | | |
Low | | | | | |
Reported | | | | | |
High | | |
R |
[Ana] |
|
A10* A11* A1 A2 A3 A4 A5 A6 A7 A8 A9 |
0.0 0.0 570 1,368 1,750 1,910 3,060 3,400 4,340 6,500 7,670 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
-127.2 -217.7 -2.1 1,468.8 1,401.8 1,841.8 3,128.5 2,633.3 3,653.5 5,386.9 6,525.2 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
-69.2 -38.8 271.3 1,551.4 1,774.9 1,867.5 3,143.0 3,406.9 4,150.5 6,129.5 7,110.8 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
-2.1 -2.1 396.4 1,579.1 1,791.4 1,958.2 3,244.9 3,463.3 4,212.5 6,272.7 7,361.0 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
-0.1 -0.1 458.3 1,639.8 2,003.7 2,020.3 3,332.3 3,490.2 4,337.1 6,617.9 7,524.3 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
9.0 0 0
556.1 1,783.9 2,134.4 2,056.1 3,461.6 4,012.9 4,640.0 7,131.9 7,544.7 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
- - 0.695 1.154 1.024 1.025 1.060 1.019 0.971 0.965 0.960 |
Si,Ca Ca MA Ca Sr,Ca Sr,Si Sr Sr,MA Fe,Si Fe,MA Si |
Mean recovery A1 to A9 = 0.986 CV = 0.126 |
* Samples A10 and A11 were blanks. Negative µg PC results can occur for samples with counts
near the intercept of the calibration curve. They are presented here for descriptive purposes only.
Quality assurance (QA) samples:
The following six QA samples SRM 637 standards tat had been stored 60 days on a laboratory bench:
QA |
Theor. |
| |
---------------- µg PC Found -------------- |
| |
Sample |
Wt.(µg) | | |
Low | | | | | |
Reported | | | | | |
High | | |
R |
[Ana] |
|
AA1 AA2 AA3 AA4 AA5 AA6 |
694 1,103 2,242 3,846 4,817 5,793 |
|
578.2 840.9 1,891.7 3,333.7 4,367.3 5,290.6 |
|
621.1 881.0 2,204.5 3,820.7 4,494.6 5,395.6 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
732.6 970.6 2,295.0 3,843.5 4,646.4 5,413.1 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
780.9 1,033.6 2,486.7 3,909.4 4,748.7 5,465.7 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
819.2 1,118.5 2.495.4 4,332.8 4,906.6 5,467.2 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
1.056 0.880 1.024 0.999 0.965 0.934 |
Si,MA Fe,Sr Ca,Si MA,Fe MA,Fe MA |
Mean recovery QA = 0.976 CV = 0.065 |
Table 1 SRM 637 - Recoveries
SRM 637 Humid Air (240 min, 80% RH) Spiked Samples: |
Air |
Theor. |
| |
------------------ µg PC Found ---------------- |
| |
Sample |
Wt.(µg) | | |
Low | | | | | |
Reported | | | | | |
High | | |
R |
[Ana] |
|
T1* T2* T7 T4 T5 T9 T3 T6 T8 |
0.0 0.0 918 1,402 1,419 2,130 2,796 2,931 2,940 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
-217.7 -135.8 944.7 1,059.4 1,024.7 1,744.2 2,302.0 2,367.3 2,465.4 |
|
-125.4 -8.6 951.4 1,292.5 1,188.0 1,939.4 2,329.0 2,469.0 2,664.7 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
-2.1 -2.1 1,063.2 1,324.6 1,213.1 2,062.3 2,455.2 2,541.5 3,000.6 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
7.7 -0.1 1,373.6 1,399.8 1,281.2 2,126.8 2,545.7 2,765.4 3,006.3 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
9.0 -0 0
1,593.5 1,585.3 1,364.4 2,275.2 2,809.7 2,797.8 3,023.2 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
- - 1.158 0.945 0.855 0.968 0.878 0.867 1.021 |
Sr,Si Ca Fe Ca,Si Si Si,Sr MA,Si MA Fe,Si |
Mean recovery T3 to T9 = 0.956 CV = 0.113 |
* Samples T1 and T2 were blanks. Negative µg PC results can occur for samples with counts
near the intercept of the calibration curve. They are presented here for descriptive purposes only.
Quality assurance samples:
The following four QA samples consisted of re-analysis of two recent SRM 637
standards used in the calibrations above, a re-analysis of sample A4 above, and a
new 2204 µg calibration standard TT4:
QA |
Theor. |
| |
---------------- µg PC Found ---------------- |
| |
Sample |
Wt.(µg) | | |
Low | | | | | |
Reported | | | | | |
High | | |
R |
[Ana] |
|
TT1 TT2 TT3 TT4 |
1,034 1,910 2,204 3,395 |
|
879.7 1,081.4 1,598.6 2,477.5 |
|
895.1 1,564.6 1,917.3 2,766.8 |
|
967.6 1,804.4 2,140.8 3,253.3 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
982.8 1,896.6 2,228.4 3,333.3 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
1,238.9 1,969.1 2,307.7 3,351.1 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
0.936 0.945 0.971 0.958 |
MA,Sr MA,Si Si,MA Si |
Mean recovery QA = 0.952 CV = 0.016 |
Table 2 SRM 635 - Recoveries
SRM 635 Dry Air Spiked Samples: |
Air |
Theor. |
| |
----------------- µg PC Found --------------- |
| |
Sample |
Wt.(µg) | | |
Low | | | | | |
Reported | | | | | |
High | | |
R |
[Ana] |
|
B11* B12* B1 B2 B3 B4 B5 B6 B7 B8 B9 B10 |
0.0 0.0 851 888 1,093 2,395 3,058 3,117 3,656 3,879 7,314 7,345 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
|
-0 0
-0.1 835.2 820.0 1,148.6 2,384.4 2,939.5 3,237.6 3,265.5 3,601.6 6,898.9 6,208.4 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
5.5 -0 0
901.1 864.9 1,168.6 2,390.1 2,944.1 3,301.7 3,497.6 3,960.7 7,184.2 7,110.0 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
7.2 0.4 976.4 898.5 1,245.5 2,414.5 3,211.9 3,366.8 3,504.7 4,171.5 7,262.7 7,349.5 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
|
70.6 30.8 1,000.4 910.9 1,304.4 2,557.4 3,302.3 3,498.1 3,704.3 4,455.0 7,486.4 7,684.7 |
|
650.6 38.7 1,055.4 1,102.7 1,365.6 2,758.4 3,481.2 3,650.7 3,731.0 5,038.4 7,619.7 7,925.7 |
|
- - 1.147 1.012 1.140 1.008 1.050 1.080 0.959 1.075 0.993 1.001 |
Sr Sr Fe,Ca Si,Ca Fe Ca,MA Sr,Ca Sr Ca,Si Sr,Fe Fe,Si MA,Ca |
Mean recovery B1 to B10 = 1.046 CV = 0.060 |
* Samples B11 and B12 are blanks. Negative µg PC results can occur for samples with
counts near the intercept of the calibration curve. They are presented here for descriptive purposes only.
Quality assurance samples:
The following six QA samples are SRM 635 standards that had been stored 60 days on a laboratory bench:
QA |
Theor. |
| |
---------------- µg PC Found --------------- |
| |
Sample |
Wt.(µg) | | |
Low | | | | | |
Reported | | | | | |
High | | |
R |
[Ana] |
|
BB1 BB2 BB3 BB4 BB5 BB6 |
623 1,088 2,172 2,964 4,644 5,839 |
|
615.0 874.6 2,119.3 2,515.9 3,454.5 3,848.1 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
669.1 915.0 2,205.1 2,699.2 4,267.8 4,955.4 |
|
730.6 946.8 2,259.1 2,706.6 4,343.5 5,039.8 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
763.8 1,092.2 2,309.1 2,735.7 4,440.6 5,939.5 |
|
868.4 1,121.3 2,311.5 2,763.5 4,478.8 >6,412.4 |
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif)
![theoretical weight](https://webarchive.library.unt.edu/eot2008/20081106065008im_/http://www.osha.gov/dts/sltc/methods/inorganic/id207/id207fig05.gif) |
1.173 0.870 1.040 0.913 0.935 0.863 |
Si,Ca Fe,Sr Sr,MA Sr Fe Ca,Fe |
Mean recovery QA = 0.966 CV = 0.124 |
Note: The "High" result for sample BB6 is above the useful calibration range.
This outlier is automatically excluded by use of the median value.
- An evaluation of relative bias among the five different analyses was performed. The tally
or count of samples having a particular analysis (Si to Sr) at each of the five rank locations
(Low to High) was determined. These are listed in the first six columns of
Table 3 below. The apparent bias suggested by these tallies is listed
in the "Apparent Bias" column.
An assessment was made to determine whether any of the five analyses tended to be more reliable
than the others. This was performed in the following manner: For each sample, the identity of
the two analyses which bracketed the theoretical result (shown in "[Ana]" columns of Tables 1
and 2 above) was determined. The tally for each of the analyses that bracketed the theoretical
result was increased by one for each sample. For example, the Si tally was increased by one
for each sample having a Si result ranked adjacent to the theoretical result. The process was
analogous for the Ca, MA, Fe, and Sr analyses. There were instances where two results did not
bracket the theoretical value; for these samples, the tally for the closest analysis was
increased by two so that each sample would be given equal overall weighing in the tallies. The
number of times a particular analysis bracketed the theoretical value is shown in the "Tally
Bracket" column of Table 3 below:
Table 3
32 Air Samples and Blanks: |
|
| |
------------------ Tally ----------------- |
| |
Apparent |
Tally |
Analysis | | |
Low | | | | | |
Middle * | | | | | |
High | | |
Bias |
Bracket |
|
Si Ca MA Fe Sr Total |
|
1 2 1 9 19 32 |
|
3 11 6 8 4 32 |
|
4 12 7 4 5 32 |
|
12 3 8 8 1 32 |
|
12 4 10 3 3 32 |
|
high low-middle high low-middle low |
15 15 9 10 15 64 |
16 QA samples: |
|
| |
-------------------- Tally ------------------- |
| |
Apparent |
Tally |
Analysis | | |
Low | | | | | |
Middle * | | | | | |
High | | |
Bias |
Bracket |
|
Si Ca MA Fe Sr Total |
|
6 3 0 2 5 16 |
|
2 6 3 4 1 16 |
|
4 4 5 2 1 16 |
|
1 2 5 5 3 16 |
|
3 1 3 3 6 16 |
|
low low-middle high-middle middle high & low |
7 3 9 7 6 32 |
Total 48 Air, Blank, and QA Samples: |
|
| |
--------------------- Tally ------------------ |
| |
Apparent |
Tally |
Analysis | | |
Low | | | | | |
Middle * | | | | | |
High | | |
Bias |
Bracket |
|
Si Ca MA Fe Sr Total |
|
7 5 1 11 24 48 |
|
5 17 9 12 5 48 |
|
8 16 12 6 6 48 |
|
13 5 13 13 4 48 |
|
15 5 13 6 9 48 |
|
high low-middle high low-middle low |
22 18 18 17 21 96 |
* Reported value
As the "Tally Bracket" results in Table 3 indicate, no single element was optimum for
quantitating PC. Individually, the analyses for an element may show an apparent bias in the
rank, but the median results of all the analytes taken together gave the most representative
estimate of the quantity of PC present in the samples.
|
4.5. Recovery and Coefficients of Variation
For the simulated "air" samples, the recovery R (Found/Taken) and CV data were calculated based
on the medians of the five different analyses described above. (CV for quality assurance
samples are also listed separately below.) The theoretical weight of each simulated "air"
sample was determined based on the net weight. Because air samples were simulated and the
sampling pump was used for movement of particulate rather than for delivery of a specific
volume of air, a 5% pump error estimate was included in the calculation of the total
coefficient of variation (CVT) using the following equation:
CVT = [ (CV)2 + (0.05)2]½
Spiked "Air" Samples:
SRM
|
Mass range (mg)
|
n
|
RH (%)
|
R
|
CV
|
CVT
|
|
635 637 637 |
0.9 to 7.3 0.6 to 7.7 0.9 to 2.9 |
10 9 7 |
Dry Dry 80 |
1.046 0.986 0.956 |
0.060 0.126 0.113 |
0.078 0.136 0.124 |
|
Combined results from above: |
SRMs
|
Mass range (mg)
|
n
|
R
|
CV
|
CVT
|
|
635 & 637 |
0.6 to 7.7 |
26 |
1.001 |
0.103 |
0.114 |
Quality assurance samples analyzed:
Re-analysis of standards stored for two months in petri dishes on laboratory bench
(These were not stored in a desiccator.):
SRM
|
Mass range (mg)
|
n
|
R
|
CV
|
|
635 637 |
0.6 to 5.8 0.7 to 5.8 |
6 6 |
0.966 0.976 |
0.124 0.065 |
Analysis of a spiked membrane filter sample, re-analysis of an 80% RH sample, and
re-analysis of two standards:
SRM
|
Mass range (mg)
|
n
|
R
|
CV
|
|
637 | 1.0 to 3.4 | 4 | 0.952 | 0.016 |
Grand summary of all "air" and quality assurance sample results:
SRM
|
Mass range (mg)
|
n
|
R
|
CV
|
|
635 & 637 | 0.6 to 7.7 | 42 | 0.980 | 0.104 |
4.6. Overall Error
Overall error (OE) is defined as a combination of the contributions of bias and imprecision in
recovery and is expressed as a percentage:
OE = ± [ | R - 1 | + 2(CVT) ] 100%
For the "air" samples:
SRM
|
Mass range (mg)
|
n
|
RH (%)
|
OE (%)
|
|
635 637 637 |
0.9 to 7.3 0.6 to 7.7 0.9 to 2.9 |
10 9 7 |
Dry Dry 80 |
±20.2 ±28.6 ±29.2 |
Combined results from above: |
SRMs
|
Mass range (mg)
|
n
|
OE (%)
|
|
635 & 637 | 0.6 to 7.7 | 26 | ±22.9 |
4.7. Storage Tests and 100% RH Tests of Prepared Samples
4.7.1. Procedure:
- Standards deposited on Ag membrane filters were reanalyzed after being stored in petri
dishes on a laboratory bench for 60 d (AA and BB samples shown in Tables 1 and 2,
Section 4.4.2.).
- High humidity experiments were also performed to determine the effect of 48-h
exposure to 100% RH on SRM 637 standards. These were 6-mg samples on Ag membrane
filters (fixed and unfixed with parlodion). During the exposure, the membrane filters were kept
in upright positions in XRD sample holders (PW1813/26 with aluminum back plates, Philips) so
that any change in intensity would not be due to sample handling.
4.7.2. Results:
- The re-analysis of standards stored on a laboratory bench for 60 d did not indicate storage problems.
- The experiments performed on SRM 637 standards exposed to 100% RH resulted in large
decreases in XRD intensity (about 30 to 40%), pitting and corrosion of the aluminum back plates
of the sample holders, and the appearance of a light-colored dust adhering to the
backs of the Ag membrane filters. Presumably, Ca(OH)2, leached from
the sample to react with the aluminum back plates. Although 100% RH is not common in controlled
environments such as analytical labs, this experiment points out that prepared samples should
not be stored in aluminum sample holders unless placed in a desiccator.
4.8. Conclusions
Portland cement dust consists of a variable and complex mixture of component phases. At the
time of this writing, the total dust PC PEL is not limited to a legally defined
particle-size distribution. Industrial exposures to PC aerosols vary with respect
to both compositions and particle-size distributions. Thin-film XRF
techniques are sensitive to both these effects. As a consequence, the compositional variability
is echoed in the analytical results. In order to minimize variability in the reported result,
the following approach was taken:
- A representative bulk sample of PC from the workplace being sampled is sieved to a
particle-size range that is typical of PC aerosols and is used to prepare standards.
- The median result of five different analytes measured by XRF is used to provide a
consensus estimate in order to resolve the effect of varying aerosol composition during sampling.
- The presence of PC is confirmed qualitatively by matching the XRD patterns of the air sample
to the XRD "fingerprint" for PC phases.
Impurities such as CaSO4 and uncombined CaO readily absorb moisture
from the air. This evaluation indicated that minimal humidity effects are expected during
sampling at <80% RH. Storage of prepared samples for 60 d in petri dishes on a
laboratory bench also indicated no significant sensitivity to the ambient conditions in the
laboratory; however, prepared samples exposed to 100% RH for 48 h were significantly affected.
These latter samples were on Ag membrane filters and were contained in sample holders. Therefore,
it is prudent to take reasonable precautions to minimize sample storage in humid air.
OSHA Method ID-207 is suitable as an adjunct to gravimetric field evaluations for the
determination of PC exposures in workplace atmospheres.
5. References
5.1. Kirk, R.E. and D.F. Othmer: Encyclopedia of Chemical
Technology. 3rd ed., Vol. 5. New York: John Wiley & Sons, 1979. pp. 163-193.
5.2. National Institute Standards and Technology: Standard
Reference Materials: Portland Cement Chemical Composition Standards (Blending, Packaging, and
Testing) (National Bureau of Standards, Special Publication 260-110, 103 pages
CODEN:XNBSAV) by R. Keith Kirby and Howard M. Kanare. Washington, D.C.: U.S. Government
Printing Office, 1988.
5.3. American Society for Testing and Materials: 1978 Annual Book of
ASTM Standards; Part 14. Philadelphia, PA: ASTM, 1978. pp. 104-110.
5.4. American Conference of Governmental Industrial Hygienists:
Documentation of the Threshold Limit Values and Biological Exposure Indices, 5th ed.
Cincinnati, OH: American Conference of Governmental Industrial Hygienists (ACGIH), 1986. p. 494.
5.5. "Air Contaminants; Final Rule": Federal Register 54:12 (19 Jan. 1989).
pp. 2598-2599.
5.6. Sisler, H.H., C.A. VanderWerf, and A.W. Davidson:
College Chemistry A Systematic Approach, 2nd ed. New York: The Macmillan Co., 1961. p. 548.
5.7. Occupational Safety and Health Administration - Salt Lake Technical Center:
OSHA Analytical Methods Manual (USDOL-OSHA-SLTC Method and Backup Report No. ID-142).
Cincinnati, OH: American Conference of Governmental Industrial Hygienists (In publication).
5.8. Jugovic, Z.T.: Spectrophotometric and EDTA Methods for Rapid Analysis of Hydraulic Cement.
ASTM Special Technical Publication: 985:15-25 (1988).
5.9. Scott, E.H.: Atomic Absorption Methods for Analysis of Portland Cement.
ASTM Special Technical Publication: 985:57-72 (1988).
5.10. Occupational Safety and Health Administration - Salt Lake Technical Center:
Personal communication to West Germany's Saarbergwerke Aktiengesellschaft regarding "Report on
Saarberg Portland Cement Analyses." January 30, 1990, Salt Lake City, UT: USDOL-OSHA-SLTC, 1990.
5.11. National Institute for Occupational Safety and Health and Occupational Safety and Health
Administration: Occupational Safety Guidelines for Chemical Hazards, Occupational Health
Guideline for Portland Cement (September, 1978) [DHHS (NIOSH) Publication No. 81-123, 19811.
5.12. Occupational Safety and Health Administration - Salt Lake Technical Center:
Standard Operating Procedure, Inorganic Analysis by X-ray Fluorescence Spectrometry
(Semiguant-XRF). Salt Lake City, UT: USDOL-OSHA-SLTC, 1989.
5.13. Silverman, L., C.E. Billings, and H.W. First: \
Particle Size Analysis in Industrial Hygiene, New York, Academic Press, 1971. pp. 13-16.
5.14. Bertin, B.P.: Principles and Practice of X-ray Spectrometric Analysis.
2nd ed. New York: Plenum Press, 1975. pp. 529 and 738.
5.15. Birks, L.S.: X-ray Spectrochemical Analysis.
2nd ed. New York: Interscience Publishers, 1969.
Appendix A
Suggestions for XRF Calibration Curves for PC Analysis
(The software features described below were incorporated into custom analytical software used
at the OSHA Salt Lake Technical Center.)
Least squares curve fits are commonly used to obtain calibration curves. In X-ray
calibrations, the count intensity is the dependent variable, and the mass is the independent
variable. The least squares approach minimizes the sum of the squares of the differences between
the dependent variable data and the curve. To find the best fit for PC analytes, the analyst
should evaluate power series fits for the first through fourth order curves. It is often
desirable to weight the data according to the reliability of the dependent variable. The
calibration data may be assigned weights inversely proportional to the intensity variance. The
random error in gross intensity obeys Poisson statistics and is a significant fraction of the
measurement error. The Poisson variance statistic is simply the gross intensity. For intensity
measurements with a low background, the Poisson variance statistic may be approximated by the
net intensity.
Caution: When creating PC calibration curves, do not over-weight the lower
standards; the counting error is not the only source of error in the measurement. In the
evaluation of the PC method (Section 4.), the adjusted Poisson weights
varied from 1,000 (maximum) for blanks to about 2 for the highest standard.
For the MA analysis of PC using the fluorescence X rays from the Ag membrane filter, the
weighting is not simply related to the net counts; net counts are calculated from silver line
intensities (i.e., Iblank - Isample). In the method evaluation, the Ag data were weighted
equally.
For a wide variety of PC SRMs and building construction materials encountered in the
preliminary evaluation, a monotonic positive S-shaped (sigmoidal or ogival) curve often best
described the calibration data for each analytical line. An example sigmoidal curve is shown below:
Three regions of interest are shown above:
Region 1 (low sample weights) shows reduced sensitivity as the result of two causes:
- Fine particulates may penetrate into the surface pores of the Ag membrane filter. The Ag
acts to shield particulates from a portion of the incident X rays and also absorbs a portion of
the fluorescence X rays from the particulates (shadowing).
- Profile-fitting (deconvolution) software tends to compute smaller peak widths
for low intensity peaks.
Region 2 (moderate sample weights) shows an approximately linear response to sample mass.
For layers that are only a few particles deep, the sensitivity is dependent upon the
particle-size distribution and the concentrations of all elements in the particles (the matrix).
Region 3 (high sample weights) shows reduced sensitivity due to partial absorption of both
incident and fluorescence X rays within thick dust layers.
When preparing PC calibration curves, the analyst must decide upon the most appropriate fit.
The fit selected should be monotonic (have a single-valued inverse) in the
analytical range. If a curve maximum is found in the range of standards suggested, the analyst
should consider reducing the analytical range, replicating standards, or trying another curve fit.
The simplest mathematical models are represented by first- or second-order
fits. First- and second-order models often provide adequate fits for analyses
experiencing small deviations from linearity. Two such instances are analyses based on the
higher-energy fluorescence X rays or analyses based on material having a large
weight fraction of small particles.
The simplest power series function that may describe a sigmoidal curve is third order.
Occasions may arise when a fourth-order fit may be the best selection.
Caution: Additional small random (non-systematic) errors due to variations in sample
preparation, etc. are expected. Although a fourth-order fit may intersect all the
data points, a lover order fit is generally preferred in order not to bias the curve fit by
these small irreproducible errors. It is a good policy to keep the mathematical model as simple as possible.
The weight of PC is determined from the inverse function of the selected power series. This is a
simple calculation for first and second-order fits. Determining the inverse of
higher-order equations is a more complex task; however, computer programs are
available to numerically solve higher-order fits in the monotonic analytical range.
Solutions to higher-order (polynomial) equations are easily determined by a successive
approximation process called binary search. In a binary search for this application, a succession
of estimates of the analyte mass is used to calculate corresponding count intensities (using
the calibration equation) until there is negligible difference between the calculated and
measured intensity. Each iteration of the search narrows the subsequent search by halving the
previous search domain. The binary search procedure is as follows (an example follows the procedure):
- The initial analytical search range must be monotonic. Determine the mass domain
(initially, about 0 to 6 mg) and calculate the mass at the center of the mass domain
(M½). The value for M½ is initially about 3 mg.
- Evaluate the polynomial at M½ in order to obtain the calculated counts (I½).
- Determine if the measured intensity (Im) is less than I½.
- If Im is not less than I½, the upper half of the
current mass domain becomes the new current mass domain. Proceed to step 6 below.
- If Im is less than I½, the lower half of the current
mass domain becomes the new current mass domain.
- The mass midway in the current mass domain becomes the new M½.
- Repeat steps 2 through 6 until there is no significant difference between
Im and I½. This takes fewer than 23 iterations.
- The last M½ obtained is the inverse function of the polynomial that gives Im.
Note: For cases where the measured counts decrease with increasing mass (e.g., Ag
counts versus PC mass), first transform the measured count data for the standards and
samples by subtracting the mean of the blank count data.
Consider the following example of the binary search procedure to find the mass corresponding
to a measurement of 5,500 counts (shown as a "+" in the figure below):
The calibration curve above approximates the following calibration data:
Mass (mg)
|
Counts
|
Weighting factor
|
0.000 1.000 2.000 3.000 4.333 6.000 |
50 1,500 3,200 6,000 8,900 10,500 |
420 14 7 4 2 2 |
The experimental data was fit by the third-order equation
I = ƒ(mass):
counts = -73.6162(mass)3 + 599.4118(mass)2 + 802.421(mass) + 51.190
The monotonic analytical range is for the mass domain 0.0000 to 6.0248 mg.
Each iteration halves the span of the mass domain; this results in the convergence to a mass
that corresponds to a calculated count intensity equal to the measured count intensity.
|
-------- Mass ---------- |
----------- Counts -------- |
|
Iteration
|
Domain (mg)
|
Mid value M½
|
Calculated I½ = ƒ (M½)
|
Measured Im
|
(I½<Im)
|
1 2 3 4 5 6 7 8 9 10 11 12 |
0.0000 to 6.0248 0.0000 to 3.0124 1.5062 to 3.0124 2.2593 to 3.0124 2.6358 to 3.0124 2.8241 to 3.0124 2.8241 to 2.9183 2.8241 to 2.8712 2.8477 to 2.8712 2.8477 to 2.8594 2.8477 to 2.8535 2.8477 to 2.8506 |
3.0124 1.5062 2.2593 2.6358 2.8241 2.9183 2.8712 2.8477 2.8594 2.8535 2.8506 2.8491 |
5,895.41 2,368.10 4,074.78 4,982.65 5,439.89 5,668.05 5,554.05 5,496.98 5,525.25 5,511.25 5,504.12 5,500.55 |
5,500 5,500 5,500 5,500 5,500 5,500 5,500 5,500 5,500 5,500 5,500 5,500 |
no yes yes yes yes no no yes no no no no |
This process can be continued to any desired precision of calculation. During 23 iterations,
the value of I½ approaches 5,500 counts and the value of M½ approaches
2.8487 mg (to five figures).
Appendix B
Typical PC X-ray Diffracton Patterns
Appendix C
Particle Size Considerations in Sampling for PC
Particles <100 µm achieve terminal velocity very quickly in still air. The terminal
velocity may be estimated from a derivation using Stokes' relation for streamline flow
(5.13.):
FR = 3p µƒ V Dp
Where: |
FR | = | viscous resistance force of the air (gm cm/sec2) |
µƒ | = | viscosity of the fluid (g/cm sec) |
V | = | velocity of particle relative to air (cm/sec) |
Dp | = | spherical particle diameter (cm) |
In free fall, this force of resistance is balanced by the gravitational force acting
on the particle. (One may neglect the force due to buoyancy because the density of air
is much less than that of PC particles.)
FR = rp p/6 (Dp)3 G
Where: |
rp | = |
density of particle (g/cm3) |
G | = | acceleration due to gravity (cm/sec2) |
Substituting:
3p µƒ V Dp = rp p/6 (Dp)3 G
Solving for V:
V = rp (Dp)2 G / (18 µƒ)
Note: G / (18 ƒ) = 3.02 × 105
for ambient air at the surface of the Earth when Dp is expressed in
cm. Use 3.02 × 10¯3 for Dp
expresses in µm.
PC phases have densities in the range 3.0 to 3.8 g/cm3.
The calculated settling rate range for 41-µm spherical particles with this
density range is 15 to 19 cm/sec.
PC particles are not spherical (5.1.). Most nonspherical particles
settle at a slightly slower rate. The worst-case deviation is about 33%
(5.13.). For nonsherical 41-µm particles of PC, the
slowest velocity range for settling out of the air would be 10 to 13 cm/sec. A stationary
volume of air 6 m high would become free of PC particles larger than 41 µm in less than 1 min.
In the case of dust exposures involving dust that is continually replenished from a source,
the particle-size distribution changes over time; the concentration of smaller
particles increases until a steady state is achieved. Particles <41 µm
would represent the greatest contribution to the dust suspended in the air.
The foregoing discussion considers only particles subject to streamline flow, but
non-streamline flow does not alter the conclusion. The largest spherical particle
falling in the streamline flow range can be estimated from (5.13.):
Dp <100 / (rp)1/3
For the density range of PC phases, the largest particles that exhibit streamline flow are in
the range of 64 to 69 µm (corresponding to 43 to 47 cm/sec). Particles larger than this
are subject to turbulent flow and clear the air at velocities faster than 47 cm/sec.
|