Crack Growth Rates and Fracture Toughness of Irradiated Austenitic Stainless Steels in BWR Environments (NUREG/CR-6960)

On this page:

Publication Information
Abstract

Download complete document

The following links on this page are to documents in Adobe Portable Document Format (PDF). See our Plugins, Viewers, and Other Tools page for more information. For successful viewing of PDF documents on our site please be sure to use the latest version of Adobe.

NUREG/CR-6960, (PDF - 6.87 MB)

Publication Information

Manuscript Completed: December 2006
Date Published: March 2008

Prepared by
O.K. Chopra and W.J. Shack

Argonne National Laboratory
Argonne, IL 60439

S. Crane, NRC Project Manager

NRC Job Code Y6388

Office of Nuclear Regulatory Research

Availability Notice

Abstract

In light water reactors, austenitic stainless steels (SSs) are used extensively as structural alloys in reactor core internal components because of their high strength, ductility, and fracture toughness. However, exposure to high levels of neutron irradiation for extended periods degrades the fracture properties of these steels by changing the material microstructure (e.g., radiation hardening) and microchemistry (e.g., radiation–induced segregation). Experimental data are presented on the fracture toughness and crack growth rates (CGRs) of wrought and cast austenitic SSs, including weld heataffected-zone materials, that were irradiated to fluence levels as high as ≈ 2 x 1021 n/cm2 (E > 1 MeV) (≈ 3 dpa) in a boiling heavy water reactor at 288-300°C. The results are compared with the data available in the literature. The effects of material composition, irradiation dose, and water chemistry on CGRs under cyclic and stress corrosion cracking conditions were determined. A superposition model was used to represent the cyclic CGRs of austenitic SSs. The effects of neutron irradiation on the fracture toughness of these steels, as well as the effects of material and irradiation conditions and test temperature, have been evaluated. A fracture toughness trend curve that bounds the existing data has been defined. The synergistic effects of thermal and radiation embrittlement of cast austenitic SS internal components have also been evaluated.

Paperwork Reduction Act Statement

This NUREG does not contain information collection requirements and, therefore, is not subject to the requirements of the Paperwork Reduction Act of 1995 (44 U.S.C. 3501 et seq.).

Public Protection Notification

The NRC may not conduct or sponsor, and a person is not required to respond to, a request for information or an information collection requirement unless the requesting document displays a current valid OMB control number.